Good Super alloy hastelloy c 276 alloy plate in stock for sale

Inconel is a group of austenitic nickel-chromium-based super alloys produced by Special Metals Corporation. Super alloys are referred to as high performance alloys that function well in environments with elevated temperatures.Super alloy INCONEL C-276 has high molybdenum content which provides the material with localized corrosion resistance like pitting. This alloy is generally known for corrosion resistance in a wide range of aggressive media. The low carbon content in this alloy helps to reduce carbide precipitation while performing welding.The following section explains in detail about super alloy INCONEL C-276.Chemical CompositionThe chemical composition of INCONEL C-276 is outlined in the following table. ElementContent (%)Molybdenum, Mo15-17Chromium, Cr14.5-16.5Cobalt, Co2.5 maxManganese, Mn1Vanadium, V0.35 maxSilicon, Si0.08 maxPhosphorus, P0.04 maxSulfur, S0.03 maxCarbon, C0.01 maxNickel. Ni62.5-67.5Physical PropertiesThe physical properties of INCONEL C-276 are tabulated below. PropertiesMetricImperialDensity8.89 g/cm30.321 lb/in3Melting point1325 °C2417 °FMechanical PropertiesThe following table shows mechanical properties of INCONEL C-276. PropertiesMetricImperialTensile strength740.5 MPa107400 psiYield strength347 MPa50300 psiElastic modulus205 GPa29700 ksiElongation at break67%67%Thermal PropertiesThe thermal properties of INCONEL C-276 are tabulated below. PropertiesMetricImperialThermal conductivity (@23°C/73.4°F)9.80 W/m-K68.0 BTU in/hr.ft².°FFabrication and Heat treatmentWeldingWeldability of INCONEL alloy C-276 is rated as good. This material can be used as-welded for most applications.Hot WorkingHot working of this alloy can be performed 870 and 1230°C (1600 and 2250°F). in case of performing heavy working, it has to be above 1090°C (2000°F).AnnealingINCONEL alloy C-276 can be annealed at 1150-1175°C (2100-2150°F) and rapidly cooled by water quenching.ApplicationsINCONEL C-276 is chiefly used in the following areas:Chemical processingPollution controlPulp and paper productionIndustrial and municipal waste treatmentRecovery of sour natural gas.Products made using INCONEL C-276 are as follows:Air pollution control components such as ducts, stack-gas re-heaters, dampers, stack liners, scrubbers, fans and fan housingsComponents required in chemical processing such as reaction vessels, heat exchangers, evaporators, and transfer piping.
Molybdenum, Mo
15-17
Chromium, Cr
14.5-16.5
Cobalt, Co
2.5 max
Manganese, Mn
1
Vanadium, V
0.35 max
Silicon, Si
0.08 max
Phosphorus, P
0.04 max
Sulfur, S
0.03 max
Carbon, C
0.01 max
Nickel. Ni
62.5-67.5
Density
8.89 g/cm3
0.321 lb/in3
Melting point
1325 °C
2417 °F
Tensile strength
740.5 MPa
107400 psi
Yield strength
347 MPa
50300 psi
Elastic modulus
205 GPa
29700 ksi
Elongation at break
67%
67%
Thermal conductivity (@23°C/73.4°F)
9.80 W/m-K	68.0 BTU in/hr.ft².°F
Molybdenum, Mo	15-17
Chromium, Cr	14.5-16.5
Cobalt, Co	2.5 max
Manganese, Mn	1
Vanadium, V	0.35 max
Silicon, Si	0.08 max
Phosphorus, P	0.04 max
Sulfur, S	0.03 max
Carbon, C	0.01 max
Nickel. Ni	62.5-67.5
Density
8.89 g/cm3	0.321 lb/in3
Melting point
1325 °C	2417 °F
Tensile strength
740.5 MPa	107400 psi
Yield strength
347 MPa	50300 psi
Elastic modulus
205 GPa	29700 ksi
Elongation at break
67%
67%
Thermal conductivity (@23°C/73.4°F)
9.80 W/m-K	68.0 BTU in/hr.ft².°F