HASTELLOY C276 is a Nickel-chromium-molybdenum wrought alloy that is considered the most versatile corrosion resistant alloy available. This alloy is resistant to the formation of grain boundary precipitates in the weld heat-affected zone, thus making it suitable for most chemical process applications in an as welded condition. Alloy C-276 also has excellent resistance to pitting, stress-corrosion cracking and oxidizing atmospheres up to 1900°F. Alloy C-276 has exceptional resistance to a wide variety of chemical environments.Chemical CompositionThe chemical composition of INCONEL C-276 is outlined in the following table. ElementContent (%)Molybdenum, Mo15-17Chromium, Cr14.5-16.5Cobalt, Co2.5 maxManganese, Mn1Vanadium, V0.35 maxSilicon, Si0.08 maxPhosphorus, P0.04 maxSulfur, S0.03 maxCarbon, C0.01 maxNickel. Ni62.5-67.5Physical PropertiesThe physical properties of INCONEL C-276 are tabulated below. PropertiesMetricImperialDensity8.89 g/cm30.321 lb/in3Melting point1325 °C2417 °FMechanical PropertiesThe following table shows mechanical properties of INCONEL C-276. PropertiesMetricImperialTensile strength740.5 MPa107400 psiYield strength347 MPa50300 psiElastic modulus205 GPa29700 ksiElongation at break67%67%Thermal PropertiesThe thermal properties of INCONEL C-276 are tabulated below. PropertiesMetricImperialThermal conductivity (@23°C/73.4°F)9.80 W/m-K68.0 BTU in/hr.ft².°FFabrication and Heat treatmentWeldingWeldability of INCONEL alloy C-276 is rated as good. This material can be used as-welded for most applications.Hot WorkingHot working of this alloy can be performed 870 and 1230°C (1600 and 2250°F). in case of performing heavy working, it has to be above 1090°C (2000°F).AnnealingINCONEL alloy C-276 can be annealed at 1150-1175°C (2100-2150°F) and rapidly cooled by water quenching.ApplicationsINCONEL C-276 is chiefly used in the following areas:Chemical processingPollution controlPulp and paper productionIndustrial and municipal waste treatmentRecovery of sour natural gas.Products made using INCONEL C-276 are as follows:Air pollution control components such as ducts, stack-gas re-heaters, dampers, stack liners, scrubbers, fans and fan housingsComponents required in chemical processing such as reaction vessels, heat exchangers, evaporators, and transfer piping.
Molybdenum, Mo
15-17
Chromium, Cr
14.5-16.5
Cobalt, Co
2.5 max
Manganese, Mn
1
Vanadium, V
0.35 max
Silicon, Si
0.08 max
Phosphorus, P
0.04 max
Sulfur, S
0.03 max
Carbon, C
0.01 max
Nickel. Ni
62.5-67.5
Density
8.89 g/cm3
0.321 lb/in3
Melting point
1325 °C
2417 °F
Tensile strength
740.5 MPa
107400 psi
Yield strength
347 MPa
50300 psi
Elastic modulus
205 GPa
29700 ksi
Elongation at break
67%
67%
Thermal conductivity (@23°C/73.4°F)
9.80 W/m-K 68.0 BTU in/hr.ft².°F
Molybdenum, Mo 15-17
Chromium, Cr 14.5-16.5
Cobalt, Co 2.5 max
Manganese, Mn 1
Vanadium, V 0.35 max
Silicon, Si 0.08 max
Phosphorus, P 0.04 max
Sulfur, S 0.03 max
Carbon, C 0.01 max
Nickel. Ni 62.5-67.5
Density
8.89 g/cm3 0.321 lb/in3
Melting point
1325 °C 2417 °F
Tensile strength
740.5 MPa 107400 psi
Yield strength
347 MPa 50300 psi
Elastic modulus
205 GPa 29700 ksi
Elongation at break
67%
67%
Thermal conductivity (@23°C/73.4°F)
9.80 W/m-K 68.0 BTU in/hr.ft².°F