factory c276 wire for spring

HASTELLOY C276 is a Nickel-chromium-molybdenum wrought alloy that is considered the most versatile corrosion resistant alloy available. This alloy is resistant to the formation of grain boundary precipitates in the weld heat-affected zone, thus making it suitable for most chemical process applications in an as welded condition. Alloy C-276 also has excellent resistance to pitting, stress-corrosion cracking and oxidizing atmospheres up to 1900°F. Alloy C-276 has exceptional resistance to a wide variety of chemical environments. Chemical Composition The chemical composition of INCONEL C-276 is outlined in the following table. Element Content (%) Molybdenum, Mo 15-17 Chromium, Cr 14.5-16.5 Cobalt, Co 2.5 max Manganese, Mn 1 Vanadium, V 0.35 max Silicon, Si 0.08 max Phosphorus, P 0.04 max Sulfur, S 0.03 max Carbon, C 0.01 max Nickel. Ni 62.5-67.5 Physical Properties The physical properties of INCONEL C-276 are tabulated below. Properties Metric Imperial Density 8.89 g/cm3 0.321 lb/in3 Melting point 1325 °C 2417 °F Mechanical Properties The following table shows mechanical properties of INCONEL C-276. Properties Metric Imperial Tensile strength 740.5 MPa 107400 psi Yield strength 347 MPa 50300 psi Elastic modulus 205 GPa 29700 ksi Elongation at break 67% 67% Thermal Properties The thermal properties of INCONEL C-276 are tabulated below. Properties Metric Imperial Thermal conductivity (@23°C/73.4°F) 9.80 W/m-K 68.0 BTU in/hr.ft².°F Fabrication and Heat treatment Welding Weldability of INCONEL alloy C-276 is rated as good. This material can be used as-welded for most applications. Hot Working Hot working of this alloy can be performed 870 and 1230°C (1600 and 2250°F). in case of performing heavy working, it has to be above 1090°C (2000°F). Annealing INCONEL alloy C-276 can be annealed at 1150-1175°C (2100-2150°F) and rapidly cooled by water quenching. Applications INCONEL C-276 is chiefly used in the following areas: Chemical processing Pollution control Pulp and paper production Industrial and municipal waste treatment Recovery of sour natural gas. Products made using INCONEL C-276 are as follows: Air pollution control components such as ducts, stack-gas re-heaters, dampers, stack liners, scrubbers, fans and fan housings Components required in chemical processing such as reaction vessels, heat exchangers, evaporators, and transfer piping.
Molybdenum, Mo
15-17
Chromium, Cr
14.5-16.5
Cobalt, Co
2.5 max
Manganese, Mn
1
Vanadium, V
0.35 max
Silicon, Si
0.08 max
Phosphorus, P
0.04 max
Sulfur, S
0.03 max
Carbon, C
0.01 max
Nickel. Ni
62.5-67.5
Density
8.89 g/cm3
0.321 lb/in3
Melting point
1325 °C
2417 °F
Tensile strength
740.5 MPa
107400 psi
Yield strength
347 MPa
50300 psi
Elastic modulus
205 GPa
29700 ksi
Elongation at break
67%
67%
Thermal conductivity (@23°C/73.4°F)
9.80 W/m-K	68.0 BTU in/hr.ft².°F
Molybdenum, Mo	15-17
Chromium, Cr	14.5-16.5
Cobalt, Co	2.5 max
Manganese, Mn	1
Vanadium, V	0.35 max
Silicon, Si	0.08 max
Phosphorus, P	0.04 max
Sulfur, S	0.03 max
Carbon, C	0.01 max
Nickel. Ni	62.5-67.5
Density
8.89 g/cm3	0.321 lb/in3
Melting point
1325 °C	2417 °F
Tensile strength
740.5 MPa	107400 psi
Yield strength
347 MPa	50300 psi
Elastic modulus
205 GPa	29700 ksi
Elongation at break
67%
67%
Thermal conductivity (@23°C/73.4°F)
9.80 W/m-K	68.0 BTU in/hr.ft².°F

Product Tag: